Cat C32 aftercooler replacement

Amen!

I don't know if I buy that anymore. I have been maintaining one MAN 1100 HP yacht since 2011. The motors have been **** good, we haven't had to touch anything internally on the engines in the 8 years I've been dealing with her. The oil is more expensive, yeah..... but it's a 400 hour change interval if you're doing a lot of hours per year. The filter prices aren't terrible, paying around $70 a fuel filter or oil filters...… We did the 1000 hour service once during my tenure with the yacht......

I think the 1000 hour service was $16k. We have only done in once.

When you add the aftercooler replacement price to the C32's or C18's etc, then it gets costly. Especially if done every 6 years. Seems the 3412's didn't have aftercooler issues. I'm not really sure why CAT aftercoolers are only going 6 years or so. But I know of 3 rebuilds in 3 different boats because of aftercooler's leaking, 2 C18's and 1 C32.

Like Boulder GT3 said, 6 year replacement life for an aftercooler is short, I agree. Cat either has a bad design or using the wrong metal. Plus they recommend cleaning and testing every 2 years or 1000hrs, lot of $$$ every 6 years for one item.

I just finished the 1000hr on my MAN 1550's. It was about $17k and that included gear coolers and fixing a broken exhaust manifold bolt. I think I get a little break because the boat is pretty serviceable but the 1550's are the worst to do because they have two after coolers.

My point wasn't a MAN vs CAT thing though. CAT has best in class engineering, experience and capability, I just wonder why the AC's seem to be a weak point. Again, my C12's had 3 revisions and I think the predecessor 3196 had long running AC issues. The AC's just seem to be an ongoing issue.

In my opinion, it is quite unusual for an aftercooler to fail in such a short duration. If they are failing as a result of corrosion in the tubestack, either the material selection was not right or a fault in the design of the aftercooler or simply lack of galvanic protection. I have seen aftercoolers on other engine makes which have been running for 10 to 15 years with absolutely no issues.

Exactly, which is what everyone else is re-iterating. Man's have no galvanic protection (zincs) yet they last and last. I've seen many other engine aftercoolers last and last. I know of one QSM 11 boat with around 700 hours that's 14 years old and aftercoolers have never been touched.

MAN s do have galvanic protection but it’s a totally different and 100 % reliable system ....transom anodes .


This is tricky to get your head around .


MAN s used a large zinc fitted to the transom submerged in the salt solution/ sea .This is permanent connected to the engine by a large earth strap .

There 24 v system to run the engines ECUs , sensors, starter motor and other stuff is isolated from the boat .

When you switch off or run there’s always a anodic protection because of the seawater circuit .Thats why the coolers or any other part with a tendency for bimetallic corrosion does NOT corrode with MAN s .


With CAT ( and few others ) they approach bimetallic corrosion on a individual basis of each wet part , by fitting a localised pencil anode .

This means a manufacturer in theory can be a little lax with suppliers as third parties in the manufacturer of out sourced parts from a different anodic / catholic electrochemical difference .


This is because the fall back is the chunk of zinc screwed in .......but for the protection to actually work from a chemistry POV there needs to be a salt solution . A salt solution for the zinc to leach out its protection.


Trouble is bad design of the CAT coolers means they can in some circumstances drain out when the engines not running leaving the protection of the zinc literally hanging in the air .

That’s what’s happening .


Summary with CAT cooler corrosion .

• wider range of electrochemically different metals in the coolers
• Drying of the zincs .

MAN make everything in house on one site inc the coolers and so there electrochemical difference of components is tiny compared to CAT

There’s never loss of Zinc continuity with the transom submerged anode system .


Litigation wise CAT are covered with the 6 y throw away part regime.


The drying out thing is also a function of the installer....relative height of the WL and cooler height etc .....hence the roulette of why some CAT coolers do leak sooner than others and others seem to last the 6 year distance ....just !



see the two anodes 4 kgs of zinc for each engine , never dries out , permanently connected.

So the Two anodic protection regimes need to be handled differently.
With MAN you don’t need to fresh water flush indeed the higher concentration of the salt solution is beneficial allowing the protective parts of the Zinc to move about and ......protect .A fresh water flush may harm the general protection gained from the stern anodes .Choking the supply of protective chemistry .

With CAT ( + other localised zinc like you geny ? ) a fresh water flush may be beneficial if the thing drains out and the local zinc hangs in the air for weeks of inactivity. A weaker residual salt solution will slow down any bimetallic corrosion.

How ever if the bimetallic potentials are massive due to huge component difference ( out sourced loss of quality control to a 3 rd party ? ) then even if the zinc is wet , ie not drained out to dry then once past a certain point a weaker salt solution be beneficial.

Hope this helps ?

Thank you for the detailed explanation. I will add, that on plane the transom zincs are out of the water and not protecting, but that is for a short period of time compared to the life of the engine.

What I can't wrap my head around is many other manufacturers do use aftercoolers like Cat does and rely on zincs on the raw water parts of the engine. The old Detroits, Cummins QSM 11's and other models, MTUs I believe and various other manufacturers and they're not having aftercooler issues or even requiring the 6 year change. I did have an after cooler leak on a 2 year old/200 hour Series 60 (D.D.) one time but we caught it soon enough before any engine damage was done. Seems like CAT has been having a lot of aftercooler issues for decades now. 3116's and 3196s in the 90's had a lot of aftercooler issues even. Meanwhile some other models like the 3412's didn't.

The localised pencil anode system can work fine as you have experienced with other manufacturers and especially generators ......if the bimetallic ness for want of a better word is not great .Ie a close as possible as many components from a electrochemical pov .
Sufficient weight of zincs , changed on spec , and importantly they stay wet , even wet if there’s been a bit ot a lot of post shut down drain down .

I guess it would be interesting to see the relative weights of the coolers / heat exchangers and pencil anodes of each manufacturer and total weight of zinc bolted to the engines .To see where CAT are with this ?

Bottom line is minimising dissimilarity between metals in contact with sea water .Suspect historically CAT have had 3 rd party quality control issues due to sloppy outsourcing.

So the engineers back at HQ can design a theoretical great heat exchanger and perhaps test the first few .....all ok ......enter a contract .....then a revolving door of techs at HQ and the ball is dropped .Damage limitation comes next ....followed by loosing a huge class action law suit .Then a cover your arse statement along the lines “ replace every 6 years “ in the service manual .
In effect making them a throw away part .

Fiammetta42. I don't think it is the dissimilar metal issue. My thought is that Cat likes to put the aftercooler right smack dab on the top of the engine, up high. My thought is the heat from the engine cooling off after running and the height, cause the seawater to drain out of the aftercooler and possibly what salt is left crystallizes and gets super concentrated. On Cummins and Volvo's and others I see the aftercooler on the side of the engine and fairly low. But, I'm not an engineer, so this is just a guess.

Based on quotes I've had for Cat is close to Man when comparing the same service and then you add the 6 year ac replacement plus the 2year service. I had two boats with older Mans, the ac's and he's were cupronickel in good shape and original, also engines had isolated grounds that supposedly reduced galvanic problems.

Cat c12's/3196's were well known for there ac problems. A Cat mechanic said one of the main problems was the water pipes would expand and retract which could damaged the O-rings causing leaks. The ac sets directly over the valve intakes with no dams and water can be drawn into valves and cylinders.

When you say A/C problems are you talking about the after coolers. I am getting close to purchasing a 1998 Sea Ray 480 sedan Flybridge. I have a read a ton on the issues with the after coolers. Are they somehow tied into the A/C “airconditioning} I dont think so, but want to make sure. The boat itself is mint. Doing a full survey, on both engines by a Cat mechanic. Want-to make sure the after coolers have been updated.

Was referring to the aftercoolers. Get maintenance records if possible to verify status of aftercoolers.

I would agree that the root cause is along this line of thinking. Dealing with heat exchangers in another industry for over 25 years I would venture this is likely a design issue combining galvanic management, material selection (including brazing material/technique) and water flow/standing water. Very tough application, and throw in stress corrison effects from the vibration. MAN seems to have a much different approach, but even then, they too require their own disassemble and cleaning regime after 1000 hrs (and/or 2 yrs, which many extend if bore scope shows ok by reputable tech)